Matrix cracking in polymeric composites laminates: Modelling and experiments

D. T. G. Katerelos, Maria Kashtalyan, C. Soutis, C. Galiotis

Research output: Contribution to journalArticlepeer-review

50 Citations (Scopus)


Composites ability to retain functionality in the presence of damage is a crucial safety and economic issue. Generally the first damage mode in composite laminates is matrix cracking, which affects the mechanical properties of the structure long before its load-bearing capacity is exhausted. In this paper, a detailed analysis of the effect of matrix cracking on the behaviour of cross-ply [0/90](s) and unbalanced symmetric [0/45](s) glass/epoxy laminates loaded statically in tension is performed. Theoretical predictions of stiffness reduction due to damage are based on the Equivalent Constraint Model (ECM), which takes into account concurrent matrix cracking in all plies of the laminate, although matrix cracking under consideration is developing only within the off-axis ply of the laminates. The longitudinal Young's modulus predictions are compared to experimentally derived data obtained using laser Raman spectroscopy (LRS). The good agreement between predicted and measured values of the reduced longitudinal Young's modulus validates the ECM model and proves that its basic assumptions arc accurate. Thus, the predictions for all the mechanical properties by the ECM model are within a realistic range, while experimental evidence is required for further validation. (C) 2007 Elsevier Ltd. All rights reserved.

Original languageEnglish
Pages (from-to)2310-2317
Number of pages7
JournalComposites Science and Technology
Issue number12
Early online date29 Sept 2007
Publication statusPublished - Sept 2008


  • Polymer-matrix composites (PMCs)
  • Matrix cracking
  • Damage mechanics
  • Transverse cracking
  • Raman spectroscopy
  • Stiffness degradation
  • ply cracks
  • damage evolution
  • fields


Dive into the research topics of 'Matrix cracking in polymeric composites laminates: Modelling and experiments'. Together they form a unique fingerprint.

Cite this